Development of laboratory test Procedure for Prediction and Optimisation of Clinker Granulometry

In the pyro processing of cement raw mix , major attention is given to optimise and control the chemical processes resulting into formation of clinker minerals , as they directly influence cement properties. However , due consideration is not given to control the granulometry of clinker. This property is of immense importance since it determines efficient cooler operation , life of burning zone refractory and Grindability characteristics of resultant clinker .

Literature reports many test methods for prediction and assessment of clinker granulometry. However use of these methods is limited , as these methods  cannot be  practiced at plant laboratories due to lack of sophisticated infrastructure. Further these methods do not consider  parametric interrelations of clinker granulometry with compositional parameters  , which  is necessary for  optimisation.

At the authors laboratories attempts were  made to study and confirm the effect of clinker compositional parameters on melt phase and its densification characteristics,  for evolving a  laboratory test method for prediction of  clinker granulometry  , which can be implemented at plant.

The paper further highlights usefulness of the test procedure for prediction and optimistion of clinker granulometry .

8 thoughts on “Development of laboratory test Procedure for Prediction and Optimisation of Clinker Granulometry”

  1. Heya i am for the first time here. I found this board and I find It
    truly useful & it helped me out much. I hope to give something back and help others like you aided

  2. Have you ever thought about publishing an ebook or guest authoring
    on other sites? I have a blog centered on the same information you discuss and would love to have you share
    some stories/information. I know my subscribers would appreciate your work.
    If you are even remotely interested, feel free to send me
    an e-mail.

  3. Hey There. I found your blog the use of msn. This is an extremely well written article.
    I will make sure to bookmark it and return to read extra of your useful info.
    Thanks for the post. I will definitely return.

  4. Definitely believe that which you said. Your favorite
    justification appeared to be on the internet the easiest
    thing to be aware of. I say to you, I certainly get annoyed while people consider
    worries that they plainly do not know about. You managed
    to hit the nail upon the top as well as defined out the whole thing without having side-effects , people could
    take a signal. Will likely be back to get more.

  5. Magnificent goods from you, man. I’ve understand your stuff previous to and you’re just too wonderful.
    I actually like what you’ve acquired here, certainly like
    what you’re stating and the way in which you say it.
    You make it enjoyable and you still take care of to keep it wise.
    I cant wait to read much more from you. This is actually a wonderful site.

  6. Magnificent beat ! I would like to apprentice
    at the same time as you amend your web site, how could i subscribe for a weblog website?

    The account aided me a acceptable deal. I had been a little bit
    acquainted of this your broadcast offered brilliant clear idea

Leave a Reply

Your email address will not be published. Required fields are marked *